Solidator Cast (R020)

Solidator Cast material is a high resolution resin suitable for direct casting of jewellery. The resin offers very good burnout properties with an extremely low thermal expansion with only 0.1 % ash residue for direct casting. The Shore hardness is 80D.

Material properties:

Key figure	Method	Symbol	R060
Key figure	Method	Symbol	Clear
Applications			Fluid/airflow analysis, architecture, art
Physical properties
Shore hardness D	DIN EN ISO 48-4	D	85,6
Solid density	DIN EN ISO 1183-1	ρ	1.19 g/cm³
Tensile properties
Tensile module	ASTM D638, Type I	Et	2258 MPa
Tensile strength	ASTM D638, Type I	σM	46.7 MPa
Elongation at tensile strength	ASTM D638, Type I	εM	3,93 %
Elongation at break	ASTM D638, Type I	εtB	4,14 %
Bending properties
Bending modulus	ASTM D790	Ef	1991 MPa
Flexural strength	ASTM D790	σfM	64.9 MPa
Elongation in bending for flexural strength	ASTM D790	εfM	4,96 %
Elongation at break	ASTM D790	εfB	> 5.0 %
Impact resistance properties
Izod notched impact strength	ASTM D256	aiN	2.63 KJ/m² (26.6 J/m)
Thermal properties
Temperature of dimensional stability @ 0.45 N/mm²	ASTM D 648 (B)	Tf	53.5 °C
Glow wire flammability rating	DIN EN 60695-2-12	GWFI	-
Glass transition temperature	DIN EN ISO 11359	Tg	-
Linear coefficient of expansion -20°C ... 20°C	DIN EN ISO 11359	α	-
Linear coefficient of expansion 65°C ... 80°C	DIN EN ISO 11359	α	-
Curl / Vertical Distortion
Dimensional accuracy XY	Test print (100x100x6mm)		99,65%
Curl at test bar (200x20x5mm)	Vertical alignment of the print		0mm
Curl at test bar (200x20x5mm)	Horizontal alignment of the print		0.1 mm
Printing conditions: Printed on Solidator V3+, layer height 100 microns, 3min cleaned in isopropanol, compressed air cleaned, UV post-curing with Solidator Cure Box.