Solidator Dental Thermoform Resin

Solidator Dental Thermoform Resin is characterised by its high HDT value, which makes it particularly suitable for thermoforming and the production of dental splints. Thanks to its heat resistance, it retains its shape during the moulding process and ensures the precise adaptation of dental splints to the individual needs of patients.

Material properties:

Key figure	Method	Symbol	R080
Key figure	Method	Symbol	Dental thermoform
Applications			Thermoform Dental
Physical properties
Shore hardness D	DIN EN ISO 48-4	D	85
Solid density	DIN EN ISO 1183-1	ρ	1.18 g/cm³
Tensile properties
Tensile module	ASTM D638, Type I	Et	1900
Tensile strength	ASTM D638, Type I	σM	40 MPa
Elongation at tensile strength	ASTM D638, Type I	εM
Elongation at break	ASTM D638, Type I	εtB
Bending properties
Bending modulus	ASTM D790	Ef
Flexural strength	ASTM D790	σfM	95 MPa
Elongation in bending for flexural strength	ASTM D790	εfM	2900
Elongation at break	ASTM D790	εfB	> 5.0 %
Impact resistance properties
Izod notched impact strength	ASTM D256	aiN	17Y/m
Thermal properties
Temperature of dimensional stability @ 0.45 N/mm²	ASTM D 648 (B)	Tf	65°C
Glow wire flammability rating	DIN EN 60695-2-12	GWFI
Glass transition temperature	DIN EN ISO 11359	Tg
Linear coefficient of expansion -20°C ... 20°C	DIN EN ISO 11359	α
Linear coefficient of expansion 65°C ... 80°C	DIN EN ISO 11359	α
Curl / Vertical Distortion
Dimensional accuracy XY	Test print (100x100x6mm)		99,95%
Curl at test bar(200x20x5mm)	Vertical alignment of the print		0mm
Curl at test bar (200x20x5mm)	Horizontal alignment of the print		0.01 mm
Printing conditions: Printed on Solidator 8K, layer height 100 microns, 3min cleaned in isopropanol, compressed air cleaned, UV post-curing with Solidator Cure Box x